| Specification |
Test Method |
Result |
| Mechanical Properties |
| Tensile Strength |
ASTM-D-638-02A |
911 psi |
| Elongation |
ASTM-D-638-02A |
0.3 % |
| Compressive Strength |
ASTM-D-695-02A |
1100 psi |
| Flexural Strength |
ASTM-D-790-03 |
2,500 psi |
| Shear Strength |
ASTM-D-732-02 |
234 psi |
| Cantilever Beam (IZOD) Impact |
ASTM-D-256-02 E1 |
0.39 ft lb ft / inyes |
| Electrical Properties |
| Volume Resistivity @ 25°C |
MIL-STD-883E Notice 3, method 5011.4, paragraphs 3.5.8, 3.8.11.1 (Covered Under A2LA Accreditiation) |
0.38 ohm · cm |
Electrical Resistance
(in ohms) |
|
|
| Sample size |
|
3mm x 3mm x 1mm |
| Base material |
|
Plastic cap |
| Results: |
|
|
| Uncured material |
|
no reading |
Heat cured
(at 65°C for 15 minutes) |
|
0.8 ohms |
Air cured
(at room temp. for 5 hours) |
|
0.2 ohms |
Electrical Resistance
(in ohms) |
|
|
| Sample size |
|
30mm x 25mm x 1mm |
| Base material |
|
Fiber glass epoxy |
| Results: |
|
no reading |
| Uncured material |
|
no reading |
Heat cured
(at 65°C for 15 minutes) |
|
2.5 ohms |
Air cured
(at room temp. for 5 hours) |
|
4.0 - 6.0 ohms |
| Thermal Properties |
| Thermal Expansion |
ASTM-E-831-03
|
79.3 mm/106mm |
| Thermal Conductivity |
ASTM-C-518 |
0.578 W/m · °K |
| Glass Transition Temperature |
ASTM-D-3418 |
46 °C |
| Cure Schedule |
| Air Cure @ 24°C (75°F) |
|
4 - 5 hours |
Heat Cure:
65°C / 149°F
90°C / 194°F
125°C / 257°F
150°C / 302°F |
|
15 minutes
12 minutes
7 minutes
5 minutes |
| Working Time @ 22°C |
|
10 minutes |
| Minimum Operating Temp. |
|
-30 °C ( -22 °F ) |
| Maximum Operating Temp. |
|
150 °C ( 302 °F ) |
| General Specifications |
| Mixing Ratio |
|
1:1 |
| Density |
ASTM-D-256-02 E1 |
2.34 g/cm3 |
| Color (cured material) |
|
Silver Grey |
| Outgassing Properties |
| TML (Total Mass Loss) in % |
WVR ( Water vapour Regain) in %
|
Collected Volatile Condensable Material (CVCM) in % |
| 0.06 |
0.06 |
0.1 |